P S P – 0 1
 
Equivalent Specification  (35NiCrMo)
 
C.E.=C+ Mn +Cr+Mo+V + Ni+Cu = 0.88max
         6       5        15
 
Mechanical Property
Tensile
(Mpa)
Yield point
(Mpa)
Elongation
(%)
Reduction
(%)
Charpy V@
0(J)
Hardness
HB
830
660
14
30
60J
248-340
 
P S P – 0 2
 
Equivalent Specification  (ZG275-485H)
 
C.E.=C+ Mn +Cr+Mo+V + Ni+Cu = 0.46max
         6       5        15
 
Mechanical Property
Tensile
(Mpa)
Yield point
(Mpa)
Elongation
(%)
Reduction
(%)
CharpyV@
-10(J)
Hardness
HB
485
275
20
35
22
 
 
P S P – 0 3
 
Equivalent Specification (ASTM GR90-60)
 
C.E.=C+ Mn +Cr+Mo+V + Ni+Cu = 0.65max
         6       5        15
 
Mechanical Property
Tensile
(Mpa)
Yield point
(Mpa)
Elongation
(%)
Reduction
(%)
Charpy V@
-20(J)
Hardness
HB
620
415
20
40
34
187-241
 
 
 
P S P – 0 4
 
Equivalent Specification ( ASTM GR 95-65)
 
C.E.=C+ Mn +Cr+Mo+V + Ni+Cu = 0.65max
         6       5        15
 
Mechanical Property
Tensile
(Mpa)
Yield point
(Mpa)
Elongation
(%)
Reduction
(%)
Charpy V@
-30(J)
Hardness
HB
655
448
17
35
34
197-241
 
P S P – 0 5
 
Equivalent Specification  ( ASTM GR 135-125 )
 
C.E.=C+ Mn +Cr+Mo+V + Ni+Cu = 0.90max
         6       5        15
 
Mechanical Property
Tensile
(Mpa)
Yield point
(Mpa)
Elongation
(%)
Reduction
(%)
Charpy V@
 
Hardness
HB
930min
860min
9min
22min
Not required
301--364
 
P S P – 0 6
Equivalent Specification   (SCMn2A)
 
C.E.=C+ Mn +Cr+Mo+V + Ni+Cu = 0.62max
         6       5        15
 
Mechanical Property
Tensile
(Mpa)
Yield point
(Mpa)
Elongation
(%)
Reduction
(%)
Charpy V@
10(J)
Hardness
HB
590 min
345min
16min
35min
22
163